Naziv vsebine

STABILIT AQUA
agent for solidifying loose gravel, sand, wood chips, bark, and similar decorative materials in bulk.
SAMSOPUR 1K-6 D4
Single-component adhesive designed for bonding dry and wet wood, wooden elements, window frames, staircases, as well as for bonding wood with foam polystyrene, mineral and glass wool, PUR foam, cardboard.
CHOOSING THE RIGHT EPOXY RESIN
When considering which type of resin to use, several questions come to mind. We try to answer them all in this post.
HARTOL LUX hard-drying oil
Oil for kitchen countertops, tables, and other load-bearing interior surfaces.
LAMEPOX 23 epoxy laminating resin 1230 g
LAMEPOX 23 epoxy laminating resin 1000 + 230 g
LAMEPOX 23 epoxy laminating resin 1230 g
LAMEPOX 23 epoxy laminating resin 1000 + 230 g

LAMEPOX 23 epoxy laminating resin 1000 + 230 g

High performance general purpose epoxy laminating resin used in wet-lay or vacuum bagging glass fibre, Kevlar / aramid or carbon fibre laminations.
Tax rate
22 %
Price with VAT:
26,58 €
ADD TO CART

LAMEPOX 23

 

High performance general purpose epoxy laminating resin for use in wet-lay or vacuum bagging glass fibre, Kevlar or carbon fibre lamination.

 

Lamepox 23 is specifically designed for simple use in resin/fiberglass composite construction.
It is exceptionally compatible in wood/fiberglass/epoxy composites.
Lamepox 23 is unfilled, has low viscosity, is odorless and cures at room temperature.

 

Mixing ratio: 100:23

Pot life: 130-140 minutes

For best mixing we recommend that Part A and Part B are thoroughly mixed in one container, and then put into a second container and mixed again with a new mixing stick or a clean paddle blade. This will ensure that no unmixed residue contaminates the final application mix.

 

Cured epoxy displays exceptional physical and performance properties. It can be sanded, shaped, machined, drilled, tapped and painted.

 

Lamepox 23 is also very convenient for impregnation of rotted wood.
Deep penetration of epoxy into rotted wood makes the wood hard and stable.

Flexural strength at 20˚C after 1 day
150 N/mm2
Compressive strength at 20˚C
111 MPa
Pot life
100 g / 90 min
Mixing ratio A:B
100:23 (WEIGHT)
Tensile strength
81 MPa
Mixture viscosity after 5 min at 25˚C
500 - 600 mPa.s
Elongation at break
6 %
Glass transition temperature ˚C (Tg)
150

Related products

    EPOX 210 casting epoxy resin 1,5 kg
    Transparent, low viscosity casting epoxy resin.
    Price with VAT:
    27,25 €
    STONIT mineral stone-like casting material 5,91 kg
    STONIT is a high-quality inorganic casting material, suitable for the production of weather-resistant products similar to natural stone. It can be pigmented with inorganic alkali resistant pigments.
    Price with VAT:
    23,18 €
    VIWOOD resin for wood/plastic composites  10 + 5  kg
    High strength polymer resin for restoration/conservation of wood and for production of attractive wood-plastic composites.
    Price with VAT:
    229,56 €
    ECOSTON ceramic casting powder 5 kg
    Porcelain-like mass for casting into molds.
    Price with VAT:
    22,33 €
    EPOLIV 5000  self-levelling industrial flooring material 20 kg + 5 kg
    EPOLIV 5000 is a self-levelling polymer flooring material. Standard neutral white color (RAL 9003 ; signal white) used mainly for concrete floors.
    Price with VAT:
    307,44 €
    Cookie - Analitics
    They are used to record the website's obscurity analysis and provide us with data to provide a better user experience.
    Cookie - social
    Cookies required for plug-ins for sharing content from social media sites.
    Cookie - chat
    Cookies allow you to sign up, contact and communicate through the communication plug-in on the page.
    Cookie - marketing
    They target targeted advertising based on past user's activity on other sites.
    What are cookies?
    By visiting and using the site, you consent to the use and recording of cookies.OK Learn more about cookies